SJ102Q
Fluorine-type high alkalinity sintered flux, alkalinity is about 2.4, flux is round particle size of 10 ~ 40 mesh, loose loading ratio: 1.2-1.25g/cm3. Ac or DC reverse connection is recommended. The welding process performance is excellent, arc combustion is stable, slag removal is easy, and weld formation is beautiful. At the same time, it has the advantages of less burning loss of alloying elements, high temperature strength of surfacing metal, good corrosion resistance and wear resistance.
Scope of application:
The flux combined with H1Cr13, H2Cr13 or similar flux-cored wire is used for roll repair and surfacing of wear-resistant parts.
Welding position:
Flat fillet welding
Note:
Prior to soldering, the flux must be baked at approximately 300-350 ° C (572-662 ° F) for 2 hours.
Before welding, it is necessary to remove rust, scale, primer and other impurities on the surface of the base metal to obtain excellent welding deposited metal.
In the case of multi-layer welding, the bottom welding of groove welding requires a small current and welding speed.
New flux is added regularly to prevent flux defects and poor bead surface forming caused by flux reuse.
| SiO2+TiO2 | CaO+MgO | Al2O3+MnO | CaF2 | S | P | |
| SJ102Q | 19.35 | 34.64 | 23.87 | 21.1 | 0.023 | 0.03 |